|Title:||Effect of grain boundary misorientation on discontinuous precipitation in an AZ91 alloy|
the frequency of special-grain boundaries precipitation
|Abstract:||A scanning electron microscopy (SEM)-based electron backscatter diffraction (EBSD) analysis showed that the discontinuous precipitation (DP) reaction rate was dependent on the geometry of the grain boundary in Mg-9Al-1Zn (wt.%) alloys. DP converted a supersaturated solid solution,δ 0 (magnesium (Mg)-rich solid solution), into a two-phaseδ + γ aggregate, withδ being a precipitated Mg17Al12 (intermetallic phase) behind a migrating reaction front. The near-special grain boundary was rather inactive, whereas most of the random high-angle boundaries promoted the reaction. Prior deformation (hot rolling to achieve up to 80% thickness reduction) had no effect on Link http://link.springer.com/article/10.1007%2Fs12034-011-0345-4|
|Appears in Collections:||Publications Internationales|
Files in This Item:
|Effect of grain boundary misorientation on discontinuous precipitation in an AZ91 alloy.pdf||36,82 kB||Adobe PDF||View/Open|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.